MAJORIS GB700 - 1199
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2NLGhB_MAJORIS-GB700---1199.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GB700 - 1199 is al, 70% mineral filled polypropylene compound intended for injection moulding. The product is available in natural (GB700) and black (GB700 - 8229) but other colours can be supplied on request. GB700 - 1199 has been developed for applications where high density, good surface finish and very good flow properties are necessary. APPLICATIONS High density products, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 17.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 128 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T20P104-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Ultramid® BU50I BK-106 | BASF Corporation | Nylon 6 | Ultramid® |
| Utomer UT1CP85AC | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Clariant Nylon 6/6 PA-111G20 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Electrafil® PC NCF15 FR | Techmer Engineered Solutions | PC | Electrafil® |