VERSIFY™ 3200
| Category: | POP , Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2MZyuP_VERSIFY-3200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 3200 Plastomer is a resin with a medium melt flow rate, therefore making it a general purpose film resin. It is suitable for cast film, blown film, and BOPP and is an excellent sealant. It has excellent compatibility with PP, excellent adhesion to PE and is an useful agent to bring low seal initiation temperature, softness and temperature performance. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.876 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Total Crystallinity | 30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 94 | ||
| Shore D, Compression Molded | 44 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 840 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 131 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -23.0 | °C | Internal Method |
| Vicat Softening Temperature | 59.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 85.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 125 | ||
| 60°, 1000 µm, Compression Molded | 134 | ||
| Haze (2000 µm, Injection Molded) | 3.9 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-1195MC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| YUNTIANHUA® EF | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| Chemlon® 233 GI | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Kumho EP HAC 8270 | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| K-Bin Rigid PVC KB-2009 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |