Retpol® PDR 7386/3 UV3
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2M2pzP_Retpol-PDR-7386-3-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epalex PDR 7386/3 UV3 is a thermoplastic rubber modified polypropylene compound. It is a medium to high flow injection moulding grade developed for maximum flexibility, low surface hardness, excellent low temperature impact strength and good tear strength. It is stabilized for continuous outdoor exposure. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.30 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 37 | ||
| Shore D, 15 sec, 3.00 mm | 29 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 7.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 450 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.00 mm | No Break | ||
| 0°C, 3.00 mm | No Break | ||
| 23°C, 3.00 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 40.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP554M | LyondellBasell Industries | PP Homopolymer | Moplen |
| TRIBOCOMP® PBT GF30 TS0 | EPIC Polymers | PBT | TRIBOCOMP® |
| Chemical Resources PET08512 | Chemical Resources, Inc. | PET | Chemical Resources |
| Diakon® Frost 642 22 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Karina BLACK PVC COMPOUND -E 753D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |