Durethan® DP 2131/20 W1 901317

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2KkSqU_DurethanDP213120W1901317.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6, 20 % glass fibers, injection molding, weather stabilized, improved surface finish

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Good weather resistance Excellent appearance
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.28	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage
Vertical flow direction : 260°C, 3.00mm ¹	0.67	--	%	ISO 2577
Vertical flow direction : 120°C, 2 hours, 3.00mm ²	0.20	--	%	ISO 294-4
Flow direction : 260°C, 3.00mm ³	0.22	--	%	ISO 2577
Flow direction : 120°C, 2 hours, 3.00mm ⁴	0.070	--	%	ISO 2577

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	198	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	7600	4700	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	150	100	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	3.0	7.0	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	6400	4100	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	197	110	MPa	ISO 178/A
23°C	212	130	MPa	ISO 178
Flexural Strain at Flexural Strength ⁷(23°C)	4.1	6.4	%

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁸(> 1.00 mm)	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6, GHLR, 14-080, GF20	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 - 0.12	%	Karl Fisher

Films	Dry	Conditioned	Unit	Test Method
Film Puncture Energy				ISO 6603-2
-- ⁹	4.00	--	J	ISO 6603-2
-- ¹⁰	5.00	10.0	J	ISO 6603-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	< 10	--	kJ/m²	ISO 179/1eA
23°C	< 10	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	40	40	kJ/m²	ISO 179/1eU
23°C	45	60	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	< 10	< 10	kJ/m²	ISO 180/1A
23°C	< 10	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	30	30	kJ/m²	ISO 180/1U
23°C	30	40	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	213	--	°C	ISO 75-2/B
1.8 MPa, not annealed	215	--	°C	ISO 75-2/A
8.0 MPa, not annealed	73.0	--	°C	ISO 75-2/C
Vicat Softening Temperature	> 200	--	°C	ISO 306/B120
Melting Temperature ¹¹	222	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	2.3E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	8.9E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	2.0E+15	2.0E+13	ohms	IEC 60093
Volume Resistivity (23°C)	3.0E+15	1.0E+12	ohms·cm	IEC 60093
Relative Permittivity				IEC 60250
23°C, 100 Hz	4.10	9.34		IEC 60250
23°C, 1 MHz	3.74	4.27		IEC 60250
Dissipation Factor				IEC 60250
23°C, 100 Hz	8.0E-3	0.22		IEC 60250
23°C, 1 MHz	0.018	0.065		IEC 60250

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.800 mm	HB	--		UL 94
1.60 mm	HB	--		UL 94

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 120	°C

Note Message
1 .	150x150x3; MT 80°C; 500 Bar
2 .	150x150x3
3 .	150x150x3; MT 80°C; 500 Bar
4 .	150x150x3
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	US-FMVSS302
9 .	-30°C
10 .	23°C
11 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
RTP 201.5	RTP Company	Nylon 66	RTP
REVOLVE® N-132	Matrix Polymers	LDPE	REVOLVE®
SCANAMID 6 B32^E	Polykemi AB	Nylon 6	SCANAMID 6
Generic Polyolefin, Unspecified - Calcium Carbonate	Generic	Polyolefin, Unspecified	Generic
LNP™ LUBRILOY™ D20001 compound	SABIC Innovative Plastics	PC	LNP™ LUBRILOY™