Ultramid B3WM8 (8260 HS) BK00102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. Applications Ultramid B3WM8 (8260 HS) BK00102 is generally recommended for applications such as marine hardware, brackets, fittings, bobbins, office furniture, appliance components, and power tool housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.49 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | -- | % | ISO 62 |
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.6 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 8310 | 7700 | MPa | |
| 23°C | 6400 | 3800 | MPa | |
| 80°C | 1360 | 1400 | MPa | |
| 121°C | 970 | 1200 | MPa | |
| Tensile Strength | ASTM D638, ISO 527-2 | |||
| Break, -40°C | 135 | 135 | MPa | |
| Break, 23°C | 85.0 | 60.0 | MPa | |
| Break, 80°C | 40.0 | 35.0 | MPa | |
| Break, 121°C | 30.0 | 27.0 | MPa | |
| Tensile Elongation | ||||
| Break, -40°C | 6.0 | 5.0 | % | ASTM D638 |
| Break, 23°C | 10 | 30 | % | ASTM D638, ISO 527-2 |
| Break, 80°C | 35 | 30 | % | ASTM D638 |
| Break, 121°C | 40 | 40 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5200 | 2100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 130 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 5.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-7-121BL | Solvay Specialty Polymers | PPS | Ryton® |
| TABOREN PH 61 C 70 | SILON s.ro | PP Homopolymer | TABOREN |
| NORYL GTX™ EXNX0080 resin | SABIC Innovative Plastics | PPS+PPE | NORYL GTX™ |
| Chemlon® 125-15 MGHU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Elastron® G G301.A65.N | Elastron USA, Inc. | SEBS | Elastron® G |