Zythane® 6070A
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Zythane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2IQZ6N_Zythane-6070A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zythane 6070A is a translucent polyether--based TPU specifically formulated for injection molding applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 6070A applications include among others FDA applications, sports shoes, ski tips,other sporting goods, casters, power tools handles, good overmolded adhesion to certain EP (ex: PC, ABS, PMMA), cell phone cases, plugs, terminations, ski boot shell, animal tags, railroad pads. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | 35.0 | mg | ASTM D1044 |
| Abrasion - DIN | 28 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 12.0 | MPa | ASTM D412 |
| 300% strain | 18.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 25.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1000 | % | ASTM D412 |
| Tear Strength 1 | 44.1 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 24°C, 22 hr | 12 | % | ASTM D395B |
| 70°C, 72 hr | 30 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.0 | °C | DSC |
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 165 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 195 - 200 | °C | |
| Processing (Melt) Temp | 190 - 195 | °C | |
| Mold Temperature | 25.0 - 60.0 | °C | |
| Back Pressure | 0.500 - 1.00 | MPa | |
| Screw Speed | 60 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² |
| Injection instructions |
|---|
| Injection Speed: >.4 in/sec |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcobond® 374-74 | Chemtura | PUR-Ether | Witcobond® |
| CP PRYME® Polycarbonate PC100R | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Karina IVORY PVC COMPOUND 730D35/ 1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6233-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sumiliteresin® PR-50099 I | SBHPP | Phenolic | Sumiliteresin® |