Sarlink® TPE TPE EE-2240N-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Gd6f2_Sarlink-TPE-TPE-EE-2240N-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE TPE EE-2240N-01 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Sarlink®The main characteristics of TPE TPE EE-2240N-01 are: UV stability. Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 43 | ASTM D2240 | |
| Shaw A, 15 seconds | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 0.758 | MPa | ASTM D412 |
| Flow : 100% strain | 1.17 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 5.79 | MPa | ASTM D412 |
| Flow : Fracture | 3.59 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 910 | % | ASTM D412 |
| Flow : Fracture | 720 | % | ASTM D412 |
| Tear Strength - Across Flow | 20.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 11 | % | ASTM D395 |
| 70°C, 22 hr | 26 | % | ASTM D395 |
| 125°C, 70 hr | 78 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH400M | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Next Nylon 6 Prime Series NST35-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Bergadur™ PB40 G15 blue | PolyOne Corporation | PBT | Bergadur™ |
| Daicel PP PGM7T1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Sylvin 4200-88 Red 6287 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |