Bayfill® EA 2003 (6 pcf)

Category:	PUR-Ether/MDI , Polyurethane (Polyether, MDI)
Manufacturer:	Covestro - PUR
Trademark:	Bayfill®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2ElNcp_Bayfill-EA-2003-6-pcf-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Bayfill EA 2003 is a low-density, semirigid polyurethane foam system designed for automotive interior applications. It produces a friable foam which has the ability to absorb more energy in applications where space is limited. The Bayfill EA system is an excellent choice where occupant impact protection above the vehicle beltline is required or desired. Foams made with Bayfill EA 2003 can be incorporated into vehicle headliners and pillar covers for improved occupant protection in collisions. Because such foam is friable, it should be considered a sacrificial energy absorber and should be replaced after damage by an impact. The Bayfill EA 2003 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI) and Component B, is a polyether polyol system. As with any product, use of Bayfill EA 2003 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

General Information
Features	Low density
Uses	Foam Application in Automobile Field Car interior parts

Physical	Nominal Value	Unit
Molded Density	96.1	kg/m³

Mechanical	Nominal Value	Unit	Test Method
Compressive Strength			ASTM D1621
10% strain	0.851	MPa	ASTM D1621
50% strain	0.914	MPa	ASTM D1621
70% strain	1.25	MPa	ASTM D1621

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 250
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 mPa-s Flash Point PMCC: 199°C Part B Type: Polyol Appearance: Yellow to amber viscous liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1600 mPa-s Flash Point PMCC: 175°C Material Temperature - Isocyanate (Component A): 24 to 27°CMaterial Temperature - Polyol (Component B): 27 to 29°CMold Temperature: 54 to 60°CDemold Time: >3 minMachine Reactivity at 29 to 32°C Cream Time: 4 to 6 sec Top of Cup Time: 11 to 13 sec Gel Time: 18 to 22 sec Rise Time: 42 to 47 sec Free-Rise Density: 2.9 to 2.9 lb/ft³

Additional Information

Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 mPa-s Flash Point PMCC: 199°C Part B Type: Polyol Appearance: Yellow to amber viscous liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1600 mPa-s Flash Point PMCC: 175°C Material Temperature - Isocyanate (Component A): 24 to 27°CMaterial Temperature - Polyol (Component B): 27 to 29°CMold Temperature: 54 to 60°CDemold Time: >3 minMachine Reactivity at 29 to 32°C Cream Time: 4 to 6 sec Top of Cup Time: 11 to 13 sec Gel Time: 18 to 22 sec Rise Time: 42 to 47 sec Free-Rise Density: 2.9 to 2.9 lb/ft³

Resin Grade	Manufacturer	Category	Trademark
Matrixx TPP2B20	The Matrixx Group, Inc.	PP Copolymer	Matrixx
POLYSTONE® G black EL	Röchling Engineering Plastics SE & Co. KG	HDPE	POLYSTONE®
RTP 1005 GB 20	RTP Company	PBT	RTP
Boda BDT-H3651	Chenguang Fluoro & Silicone Elastomers Co., Ltd.	Fluorelastomer	Boda
Geon™ Vinyl Wire & Cable WR4602CL	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Wire & Cable