Amphora™ 3D Polymer AM3300
| Category: | Unspecified , Unspecified |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Amphora™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2DGMEK_Amphora3DPolymerAM3300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Amphora™ AM3300 3D polymer is a low-odor, styrene-free material uniquely suited for 3D printing enthusiasts, particularly those who need the flexibility to print within a wide processing temperature range. Amphora AM3300 has good flow properties through the printer nozzle-even at lower temperatures than some other polymers require. These properties make AM3300 more workable at a wider breadth of temperatures, producing reliable results and resulting in less waste.The model of functional aesthetics, Amphora AM3300 can be made into high-quality filament that exhibits advanced overhang ability, excellent looks, and large printing temperature range-empowering large panel of users to create durable and useful items. Amphora AM3300 is also a highly efficient polymer that can help speed up processing times. With the unique combination of a low processing temperature and an elevated temperature resistance, Amphora AM3300, can quickly print creations that are functional, durable, efficient, and attractive. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 50.0 | MPa | ASTM D638 |
| Fracture, 23°C | 35.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.5 | % | ASTM D638 |
| Fracture, 23°C | 190 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1800 | MPa | ASTM D790 |
| Flexural Strength | 67.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 38 | J/m | ASTM D256 |
| 23°C | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ASTM D4812 | |
| 23°C | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 71.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 63.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Typical Processing Conditions: Processing Melt Temperature: 210 to 240°C Heated Bed Temperature: 60°C Cooling: 0 to 100% Layer Height: 0.1 or 0.2 mm Speed: 30 to 100 mm/s Infill: As needed up to 100% Perimeter: Around 1 mm Minimal Layer Time: 4 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-2009S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Nanjing Hongrui PA66 A305 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Cheng Yu 3245 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| Karina WHITE PVC COMPOUND 653D10/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7868-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |