Lotrène® LLDPE Q2018C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | QATOFIN Company Limited |
| Trademark: | Lotrène® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Chmyo_Lotr-ne-LLDPE-Q2018C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lotrène® Q2018C can be processed at optimal output rates with moderate extrusion pressure, good web stability and gauge control on cast film machines designed for LLDPE. Lotrène® Q2018C can advantageously be blended with LDPE or other PE resins used in cast film mono extrusion or co-extrusion to improve film properties. Lotrène® Q2018C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy (20 µm) | 1.60 | J | ASTM D5748 |
| Film Puncture Force (20 µm) | 25.0 | N | ASTM D5748 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm, cast film | 165 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm, cast film | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm, extruded film | 9.70 | MPa | ASTM D882 |
| TD : Yield, 20 µm, extruded film | 9.60 | MPa | ASTM D882 |
| MD : Fracture, 20 µm, extruded film | 37.0 | MPa | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 20 µm, extruded film | 330 | % | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 670 | % | ASTM D882 |
| Dart Drop Impact 1(20 µm, Cast Film) | 35 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, cast film | 12 | g | ASTM D1922 |
| TD : 20 µm, cast film | 190 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 92 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 1.8 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Extrusion Rate | > 6.7 | m/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 250 | °C | |
| Cylinder Zone 2 Temp. | 180 - 250 | °C | |
| Cylinder Zone 3 Temp. | 180 - 250 | °C | |
| Cylinder Zone 4 Temp. | 180 - 250 | °C | |
| Cylinder Zone 5 Temp. | 180 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Die gap: >0.8 mm |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 41 G 10 | SILON s.ro | PP Homopolymer | TABOREN |
| Hostacom TSOP EM5 G43011 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Kumho PPG 3601 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |