LNP™ THERMOCOMP™ RF007SXQ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2CHLap_LNP-THERMOCOMP-RF007SXQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF007SXQ is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Hydrolysis Resistant. Also known as: LNP* THERMOCOMP* Compound RF-1007 HR HS Product reorder name: RF007SXQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 | % | |
| Across Flow : 24 hr | 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 196 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 10700 | MPa | ASTM D790 |
| Flexural Strength | 297 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3617 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MOSTEN MA 612 | UNIPETROL RPA | PP Impact Copolymer | MOSTEN |
| Karina GRAY PVC COMPOUND 830-18/5-IS-RG-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniCarb™ PC/PBT 400IM2 | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |
| SCHULABLEND® (PC/ABS) M/MB 6101 GF10 | A. Schulman Europe | PC+ABS | SCHULABLEND® |