Kaneka MUH LG5013
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Kaneka Corporation |
| Trademark: | Kaneka MUH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2A7Obr_Kaneka-MUH-LG5013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kaneka MUH LG5013 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America and is processed by injection molding. The main features of Kaneka MUH LG5013 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 42.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Flexural Strength | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 60 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 50 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 100 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 92.0 | °C | ASTM D648 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 22 | ASTM D523 |
| Additional Information |
|---|
| Coefficient of Linear Thermal Expansion, Kaneka Method, flow: 7-9 E-5 cm/cm/°CMold Shrinkage, Kaneka Method, flow, 73°F: 5-8 mil/inSpiral Flow, Kaneka Method, 482°F: 29.9 inReflective Rate, Kaneka Method, 60°, 73°F: 22 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC6G43-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| StarMediflex P 7070-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| Acrypet® IR D70 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ACRYPET® |
| BP Flex A 6310 BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| LNP™ THERMOCOMP™ DX06413H compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |