Bio-Flex® S 5630
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2A5OqL_Bio-Flex-S-5630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bio-Flex® S 5630 is a Biodegradable Polymers (Biodeg Polymers) material. It is available in Europe for injection molding or thermoforming. Primary attribute of Bio-Flex® S 5630: Eco-Friendly/Green. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 to 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 to 10.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2160 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 29.0 | MPa | ISO 527-2 |
| -- | 32.0 | MPa | ISO 527 |
| Tensile Strain (Break) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 46.0 | MPa | ISO 178 |
| Flexural Strain at Break | No Break | % | ISO 178 |
| Tensile Strain at Tensile Strength | 6.00 | vol% | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 51 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 68.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 105 | °C | ISO 306/A |
| Melting Temperature (DSC) | 140 to 160 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 130 | °C | |
| Middle Temperature | 150 | °C | |
| Front Temperature | 170 | °C | |
| Nozzle Temperature | 180 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C | |
| Adapter Temperature | 170 | °C | |
| Die Temperature | 180 | °C | |
| Take-Off Roll | 20.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® RS LC2600 BK043A | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| NEXT REPROCESSED PA6 8267-300R | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REPROCESSED |
| ACCUTECH™ CP0409HUUVV | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Andur AL 80-5 AP-FP | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Hostacom CR 250 F M C12463 | LyondellBasell Industries | PP Copolymer | Hostacom |