Durethan® BC 304 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2A0On9_DurethanBC304000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding, improved impact strength |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.06 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.06 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 260°C, 3.00mm 1 | 1.5 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.46 | -- | % | ISO 2577 |
| Flow direction : 260°C, 3.00mm 3 | 1.1 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.38 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 80.0 | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 1800 | 800 | MPa | ASTM D638 |
| 23°C | 1800 | 800 | MPa | ISO 527-2/1 |
| Tensile Strength (Yield, 23°C) | 45.0 | 35.0 | MPa | ASTM D638, ISO 527-2/50 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.5 | 30 | % | ISO 527-2/50 |
| Fracture, 23°C | > 200 | > 200 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | ||||
| 23°C | 1600 | 752 | MPa | ASTM D790 |
| 23°C 6 | 1600 | 700 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% strain, 23°C | 55.2 | 31.0 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 55.0 | 25.0 | MPa | ISO 178/A |
| 23°C 7 | 60.0 | 30.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 8(23°C) | 7.0 | 9.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GR, 14-020 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 85 | 120 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 650 | 650 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 650 | 920 | J/m | ASTM D256 |
| -30°C | 30 | 17 | kJ/m² | ISO 180/1A |
| 23°C | 70 | 100 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 125 | -- | J | ISO 6603-2 |
| 23°C | 120 | 125 | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | 90.0 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | 50.0 | -- | °C | ASTM D648 |
| 8.0 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 150 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (194°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 10 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.5E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.6E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.0E+15 | 1.0E+13 - 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 - 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | 35 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 36 | 36 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 11 | 3.30 | 9.60 | IEC 60250 | |
| 23°C, 1 MHz 12 | 3.10 | 3.50 | IEC 60250 | |
| 23°C, 100 Hz | 3.30 | 11.0 | IEC 60250 | |
| 23°C, 1 MHz | 3.00 | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.010 | 0.15 | IEC 60250 | |
| 23°C, 100 Hz | 7.0E-3 | 0.18 | IEC 60250 | |
| 23°C, 1 MHz | 0.010 0.015 | 0.060 0.090 | IEC 60250 | |
| Comparative Tracking Index | ||||
| Solution a 13 | 600 | -- | V | IEC 60112 |
| Solution B 14 | 600 | -- | V | IEC 60112 |
| -- | -- | 600 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 15 | 21 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | US-FMVSS302 |
| 10 . | 10°C/min |
| 11 . | Tinfoil Electrodes |
| 12 . | Tinfoil Electrodes |
| 13 . | Erosion depth: 1.70mm |
| 14 . | Erosion depth: 2.30mm |
| 15 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hyundai EP PA6 LS130 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| InnoPlus LL7420A | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |
| LNP™ LUBRICOMP™ CL002 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |
| Wanthane® WHT-1495B | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| OTECH PVC OE9529 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |