Bergamid™ MD A70 G50 H NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 29g3dR_Bergamid-MD-A70-G50-H-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bergamid™MD A70 G50 H NC is a polyamide 66 (nylon 66) product, which contains a 50% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 220 | MPa | ASTM D638 |
| Flexural Modulus 2 | 15000 | MPa | ASTM D790 |
| Flexural Strength 3 | 350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3705A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Moplen RP348N | PolyMirae | PP Random Copolymer | Moplen |
| Borealis PP WD955CF | Borealis AG | Polyolefin, Unspecified | Borealis PP |
| Kelon® B FR H CET/05-V2HF | LATI S.p.A. | Nylon 6 | Kelon® B |
| Petrothene® YR92126 | LyondellBasell Industries | XLPE | Petrothene® |