PENTAMID A GV25 MC25 H natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28s1sl_PENTAMIDAGV25MC25Hnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 25% glass fiber and 25% mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ISO 62 |
| Viscosity Number | 140 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 75 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 | |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66, MHR, 14-170 N, GF25+MD25 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.030 - 0.11 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 280 - 305 | °C | |
| Middle Temperature | 285 - 315 | °C | |
| Front Temperature | 290 - 305 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 90.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® TinCo 50 | A. Schulman Europe | Nylon 6 | SCHULATEC® |
| AKROMID® A4 5 EN natural (3162) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ALTECH® PS A 1000/536 AS WT1113-05 | ALBIS PLASTIC GmbH | PS (HIPS) | ALTECH® PS |
| Elastron® V V601.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| Latilon 28D G/20 | LATI S.p.A. | PC | Latilon |