TECANYL® TECANYL®
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 27otL1_TECANYL-TECANYL-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECANYL®, due to its inherent chemical composition, exhibits unusually low moisture absorption. Therefore, good electrical insulating properties are realized over a wide range of humidity and temperature conditions. Chemical attack from water, most salt solutions, acids and bases is also minimal with TECANYL®. The addition of glass fiber reinforcement enhances both the mechanical and thermal properties of the basic TECANYL® material. Made from Noryl® EN265 resin. Made from Noryl EN265 resin® exhibits a broad range of outstanding properties for applications in computers and business equipment, automotive, electrical insulation, telecommunications, appliances, electronics, and many other industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2410 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2550 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 92.4 | MPa | ASTM D790 |
| Coefficient of Friction | |||
| vs. Itself - Dynamic 1 | 0.39 | ||
| vs. Itself - Static | 0.32 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 137 | °C | |
| 1.8 MPa, Unannealed | 123 | °C | |
| Vicat Softening Temperature | 154 | °C | |
| CLTE - Flow (-18 to 60°C) | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Maximum Service Temperature | |||
| Intermittent | 110 | °C | |
| Long Term | 104 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant 2(23°C, 60 Hz) | 2.70 | ASTM D150 | |
| Dissipation Factor (23°C, 60 Hz) | 7.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL CE 02 S 22 T0 | RIALTI Srl | PP Impact Copolymer | RIALFILL |
| TAIRILAC AG1000 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Durethan® BM 40 X H2.0 EF 900116 | LANXESS GmbH | Nylon 6 | Durethan® |
| Gallonprene® GP420-7002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Garaflex™ G 7765-A5R NATURAL | AlphaGary | TPE | Garaflex™ G |