BJB Polyurethane TC-889 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 25PwGo_BJB-Polyurethane-TC-889-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-889 A/B incorporates a non-mercury based catalyst system that produces a tough 80 shore D material with a 2.5 minute work time. This system can be used to hand pour electronic housing, models of all kinds, and point of purchase items. This system is also available in a 20-minute work time (TC-892), 12-minute work time (TC-891), and a 5-minute work time (TC-890). PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.04 | g/cm³ | |
| -- | 1.14 | g/cm³ | |
| -- 2 | 1.18 | g/cm³ | |
| Specific Volume | 0.903 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time 3(25°C) | 2.5 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.60 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 90.6 | °C | |
| 1.8 MPa, Unannealed | 80.6 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 88 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 830 | cP | |
| 25°C 5 | 725 | cP | |
| 25°C 6 | 325 | cP | |
| Demold Time (25°C) | 30 to 45 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Mixed |
| 5 . | Part B |
| 6 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201.3 HS | RTP Company | Nylon 66 | RTP |
| Sanren M2500CD (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Beetle® PP809M | Teknor Apex Company (Chem Polymer) | PP Homopolymer | Beetle® |
| KEBAFLEX® S 35 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| Karina NATURAL PVC COMPOUND -E 550-25/ 1-AY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |