TOTAL Polyethylene Lumicene® M 3410 EP (EU) Datasheet,MDPE,TOTAL Refining & Chemicals-SHANGHAI SUSHENG

Message
Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer. Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film.

General Information
Additive	Antioxidant Processing Aid
Features	Good Heat Seal Good Tear Strength Heat Sealable Hexene Comonomer High Clarity High Gloss High Stiffness Puncture Resistant
Uses	Bags Blending Consumer Applications Film Food Packaging Heavy-duty Bags Laminates Multilayer Film Packaging Shrink Wrap
Agency Ratings	EC 1907/2006 (REACH)
Forms	Pellets
Processing Method	Blown Film Coextrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.934	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)
190°C/2.16 kg	0.90	g/10 min	ASTM D1238, ISO 1133
190°C/21.6 kg	30	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (vs. Itself - Static, Blown Film)	0.40		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25 to 41	µm
Secant Modulus			ASTM D882A
1% Secant, MD : Blown Film	365	MPa
1% Secant, TD : 25 µm, Blown Film	386	MPa
Tensile Stress
MD : Yield, 40 µm, Blown Film	17.0	MPa	ISO 527-3
TD : Yield, 40 µm, Blown Film	18.0	MPa	ISO 527-3
MD : Break, 25 µm, Blown Film	44.1	MPa	ASTM D882A
TD : Break, 25 µm, Blown Film	42.1	MPa	ASTM D882A
MD : Break, 40 µm, Blown Film	47.0	MPa	ISO 527-3
TD : Break, 40 µm, Blown Film	43.0	MPa	ISO 527-3
Tensile Elongation
MD : Break, 25 µm, Blown Film	400	%	ASTM D882A
TD : Break, 25 µm, Blown Film	650	%	ASTM D882A
MD : Break, 40 µm, Blown Film	630	%	ISO 527-3
TD : Break, 40 µm, Blown Film	700	%	ISO 527-3
Dart Drop Impact
25 µm, Blown Film	60	g	ASTM D1709A
40 µm, Blown Film	100	g	ISO 7765-1
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, Blown Film	55	g
TD : 25 µm, Blown Film	400	g
Seal Initiation Temperature	120	°C
Water Vapor Transmission	10	g/m²/24 hr	ASTM E96
Elmendorf Tear Strength ¹			ISO 6383-2
MD : 40.0 µm	20.0	kN/m
TD : 40.0 µm	100.0	kN/m

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	123	°C	ISO 306
Melting Temperature	124	°C	ISO 11357-3, ASTM D3417

Optical	Nominal Value	Unit	Test Method
Gardner Gloss (45°, 25.4 µm, Blown Film)	65		ASTM D523
Gloss (45°, 40.0 µm, Blown Film)	60		ASTM D2457
Haze
25.4 µm, Blown Film	9.0	%	ASTM D1003
40.0 µm, Blown Film	9.0	%	ISO 14782

Extrusion	Nominal Value	Unit
Melt Temperature	200	°C

Note Message
1 .	Blown Film

Category:	MDPE , Medium Density Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2526f3_TOTAL-Polyethylene-Lumicene-M-3410-EP-EU-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SLOVAMID® 6 NG GF 45	Plastcom	Nylon 6	SLOVAMID® 6
TABOND 2006	SILON s.ro	TPE	TABOND
ELASTOSIL® R plus 4020/50	Wacker Chemie AG	Silicone	ELASTOSIL® R plus
Karina RED PVC COMPOUND -E 530-42/179-A-IS-SD (C900)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Softell TKG 317N C12616	LyondellBasell Industries	PP Copolymer	Softell