Alkathene® LDF433
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 24hUl8_Alkathene-LDF433.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDF443 is a low density polyethylene designed for a variety of medium to heavy gauge (70 - 200µm) film applications where increased stiffness is required. LDF443 is formulated with a process stabilisation and antiblock package but contains no slip additives. Application: LDF433 is intended for use in medium to heavy gauge (70 - 200µm) film applications where increased stiffness is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.45 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.40 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 100 µm, Blown Film | 180 | MPa | |
| 2% Secant, TD : 100 µm, Blown Film | 200 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 100 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 100 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 100 µm, Blown Film | 24.0 | MPa | |
| TD : Break, 100 µm, Blown Film | 21.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 100 µm, Blown Film | 640 | % | |
| TD : Break, 100 µm, Blown Film | 820 | % | |
| Dart Drop Impact (100 µm, Blown Film) | 230 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 100.0 µm | 8 | N | |
| TD : 100.0 µm | 7 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 100 µm, Blown Film) | 62 | ASTM D2457 | |
| Haze (100 µm, Blown Film) | 14 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-MK275A | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| DIGITALWAX® RD 095 | DWS Systems | Unspecified | DIGITALWAX® |
| LEXAN™ ML7682 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| OmniLon™ PA6/6 IM8 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Iupital® A10-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |