SABIC® PPcompound 7693
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 22GGbh_SABIC-PPcompound-7693.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7693 is a very high flow mineral filled modified polypropylene. Material properties include very high flow, high stiffness and a good impact resistance. Typical applications include automotive exterior parts such as bumpers, bumper strips and exterior trim. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 7693 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 22.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 16.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 150 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 6.0 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 135 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 246M NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| DURANEX® 601SA | Polyplastics Co., Ltd. | ABS+PBT | DURANEX® |
| HiFill® PA6/6 0146 A | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| OnForce™ LFT PP-60LGF/001 Natural | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| Pibiter® N400 NERO900 | SO.F.TER. SPA | PBT | Pibiter® |