Generic PP Copolymer - Glass Fiber
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 21VZhF_Generic-PP-Copolymer---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.945 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 0.953 - 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.40 - 12 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.80 - 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.00 - 7.05 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.62 | % | ASTM D955 |
| Transverse flow : 23°C | 0.25 - 1.0 | % | ASTM D955 |
| 23°C | 0.24 - 1.2 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.010 - 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 53 - 110 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 74 - 75 | ASTM D2240 | |
| 23°C | 65 - 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1650 - 6260 | MPa | ASTM D638 |
| 23°C | 2130 - 11000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 23.6 - 80.3 | MPa | ASTM D638 |
| Yield, 23°C | 35.3 - 91.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 20.0 - 75.7 | MPa | ASTM D638 |
| Fracture, 23°C | 44.6 - 90.0 | MPa | ISO 527-2 |
| 23°C | 29.9 - 89.6 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 5.1 | % | ASTM D638 |
| Yield, 23°C | 2.4 - 6.0 | % | ISO 527-2 |
| Fracture, 23°C | 2.9 - 9.3 | % | ASTM D638 |
| Fracture, 23°C | 2.8 - 6.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1450 - 5900 | MPa | ASTM D790 |
| 23°C | 1810 - 5700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 30.3 - 114 | MPa | ASTM D790 |
| 23°C | 48.4 - 125 | MPa | ISO 178 |
| Yield, 23°C | 40.0 - 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.7 - 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 28 - 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 59 - 220 | J/m | ASTM D256 |
| 23°C | 4.0 - 25 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 210 - 810 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 0.339 - 2.98 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 140 - 160 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 110 - 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 87.7 - 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 89.3 - 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 90.0 - 160 | °C | ASTM D1525 |
| -- | 79.7 - 167 | °C | ISO 306 |
| Melting Temperature | 160 | °C | |
| CLTE - Flow | 3.0E-5 - 3.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 9.5E+15 - 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 550 - 755 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.8 - 82.9 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.20 | % | |
| Suggested Max Regrind | 21 | % | |
| Rear Temperature | 201 - 253 | °C | |
| Middle Temperature | 204 - 246 | °C | |
| Front Temperature | 191 - 247 | °C | |
| Nozzle Temperature | 188 - 247 | °C | |
| Processing (Melt) Temp | 209 - 245 | °C | |
| Mold Temperature | 32.0 - 60.0 | °C | |
| Injection Pressure | 5.52 - 90.3 | MPa | |
| Holding Pressure | 4.48 - 60.0 | MPa | |
| Back Pressure | 0.237 - 0.689 | MPa | |
| Cushion | 8.89 - 8.91 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-551U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| INSUL-PLATE™ X-28057-2HT | Sumitomo Bakelite North America, Inc. | Epoxy | INSUL-PLATE™ |
| Styrolution PS 5801 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| Elastron® G G400.A22.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina NATURAL PVC COMPOUND 730D25/1-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |