Hylex® P1007L4 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 21V27A_HylexP1007L4HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCARBONATE, LOW MELT FLOW, FDA, NO MOLD RELEASE |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 67.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 140 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 97.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 910 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 124 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marvel™ M90 | SCG Chemicals Co., Ltd. | LLDPE | Marvel™ |
| Polylink Polymer PBT-11030-GFFR | Polylink Polymers (India) Ltd. | PBT | Polylink Polymer |
| XANTAR® 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Daelim Po1y® LH-418S | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| LNP™ LUBRICOMP™ WFL34 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |