Maxxam™ PP H5 G30 grey VN8438CF UV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1xHVlT_MaxxamPPH5G30greyVN8438CFUV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 - 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 3.00 - 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Lateral flow : 23°C, 2.00mm | 0.60 - 1.2 | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 0.20 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm) | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 4.00 mm) | > 4.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 48 | kJ/m² | ISO 179 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (0.8 to 3.0mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.8 to 3.0mm) | 775 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | Bergmann Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 8001 | Formosa Plastics Corporation | HDPE | TAISOX |
| OCTAL PET DPET | OCTAL Holding & Co. | PET | OCTAL PET |
| Fainplast PVC GK 87 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fainplast PVC RI 52 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| InnoPlus HD5200B | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |