LubriOne™ SF-30CF/15T
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1x3xeK_LubriOne-SF-30CF-15T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.020 to 0.040 | % | |
| Across Flow | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 26800 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 159 | MPa | |
| Break | 159 | MPa | |
| Tensile Elongation 3(Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus 4 | 20700 | MPa | ASTM D790 |
| Flexural Strength 5 | 248 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.16 | ||
| vs. Steel - Static | 0.19 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 59 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 278 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 227 | °C | |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® DB2010CW | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Sinvicomp SFW9532D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Fainplast PVC FKT 92 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Geon™ Vinyl Rigid Extrusion 78761 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Sumikon® FM-XTK305 | SBHPP | PPS | Sumikon® |