Geon™ HTX Ultra LA426 Black 2880
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1wZGRB_Geon-HTX-Ultra-LA426-Black-2880.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™HTX Ultra LA426 Black 2880 is a polyvinyl chloride alloy (PVC alloy) product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Geon™The application areas of HTX Ultra LA426 Black 2880 include covering materials and outdoor applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 441421540000 | ASTM D4216 | |
| PVC Cell Classification | 15225 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1980 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 37.7 | MPa | ASTM D638 |
| Flexural Modulus | 2060 | MPa | ASTM D790 |
| Flexural Strength | 66.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 610 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 65.4 | J/cm | ASTM D4226 |
| 23°C 4 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 87.2 | °C | ASTM D648 |
| CLTE - Flow | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 推荐在华氏160度下将材料干燥至少2小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T10P102-00EG | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Vydyne® R413H BK07 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ATTANE™ SL 4102G | The Dow Chemical Company | ULDPE | ATTANE™ |
| Elastron® G G400.A80.N | Elastron USA, Inc. | SEBS | Elastron® G |
| LEXAN™ XHT3146 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |