| Compound based on PA6 natural first choice. Impact modified. Super tough. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 to 1.09 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 to 2600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 45.0 to 55.0 | MPa | |
| Break | 40.0 to 50.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 10 to 20 | % | |
| Break | 35 to 40 | % | |
| Flexural Modulus 1 | 1500 to 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 45.0 to 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 45 to 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 500 to 600 | J/m | ASTM D256A |
| 23°C 3 | No Break | ASTM D256 | |
| 23°C | 55 to 60 | kJ/m² | ISO 180/A |
| 23°C 4 | 50 to 60 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 160 to 170 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 165 to 175 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 to 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 195 to 205 | °C | ISO 306/A120 |
| -- | 205 to 215 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF23BL6571 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Karina ORANGE COLOR CONCENTRATE 32/1-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ EL002 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| LNP™ LUBRILOY™ RF206AXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Hypro-G™ PP-HP45 | Entec Polymers | PP Homopolymer | Hypro-G™ |