UNIBRITE® UA-1300
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | UNIBRITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1v7gOR_UNIBRITE-UA-1300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UNIBRITE® UA-1300 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 82.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 7.7E-5 | cm/cm/°C | JIS K7197 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 200 to 260 | °C | |
| Middle Temperature | 200 to 260 | °C | |
| Front Temperature | 200 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-70A HF | RTP Company | TPV | RTP |
| MFE® -11 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| Edgetek™ AT-000/000 BK022 | PolyOne Corporation | Acetal (POM) Homopolymer | Edgetek™ |
| KumhoSunny PC 3601 | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Plenco 04300 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |