LEXAN™ HP4REU resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1u1KXG_LEXAN-HP4REU-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | Internal Method | ||
| -- 1 | 0.50 to 0.70 | % | |
| 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2370 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 62.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 4 | 68.0 | MPa | ASTM D638 |
| Break | 70.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 6 | 130 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2340 | MPa | ASTM D790 |
| -- 8 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 10 | 15 | kJ/m² | ISO 179/1eA |
| 23°C 11 | 75 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 13 | 10 | kJ/m² | ISO 180/1A |
| 23°C 14 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 15 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 63.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 100 mm Span 16 | 138 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 17 | 127 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525 18 |
| -- | 143 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 140°C 19 | Pass | ||
| CLTE | |||
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*3 |
| 16 . | 120*10*4 mm |
| 17 . | 120*10*4 mm |
| 18 . | Rate B (120°C/h), Loading 2 (50 N) |
| 19 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smoothblend® ABS-1100 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Smoothblend® |
| THERMOLAST® M TM9MED (Series: MC/tl) | KRAIBURG TPE | TPE | THERMOLAST® M |
| TOTAL Polypropylene Lumicene® M 3382 MZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ALFATER XL® A75I 4GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Karina YELLOW PVC COMPOUND 752D02/101-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |