RTP 1387 HM
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1tf3S8_RTP-1387-HM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 37900 | MPa | ASTM D638 |
| Tensile Strength | 114 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 31000 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 160 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 1mil/in.The value listed as flammability, UL 94, was tested in accordance with RTP test standards.RTP 1380 HM Series materials are high modulus carbon fiber PPS. They are characterized by excellent physical properties, extremely high moduli, heat resistance and inherently flame retardant. RTP 1391 HM exhibits a modulus greater than that of aluminum with a specific gravity 40% less than aluminum. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 285 - 343 | °C | |
| Middle Temperature | 285 - 343 | °C | |
| Front Temperature | 285 - 343 | °C | |
| Mold Temperature | 65.6 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 60 - 90 | rpm | |
| Clamp Tonnage | 1.4 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PP FS3001E | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| Sylvin 8240-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Synres-Almoco SI 4554 | Synres-Almoco BV | Silicone | Synres-Almoco |
| Fainplast PVC GSK 92 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ISOTHANE® 1040AU | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |