Plavis® G40
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Comco Nylon GmbH |
| Trademark: | Plavis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1tenN4_PlavisG40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLAVIS is a super engineering plastic. PLAVIS polyimide has a unique chemical structure with some of the highest properties availiable. Nitrogen bonded to 3 carbons is the critical part of the chain and imparts the plastic with remarkable features and benefits. DAELIM makes PLAVIS isostatic molded rods have uniform properties in all directions. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D1708 | ||
| Fracture, 23°C | 56.9 | MPa | ASTM D1708 |
| Fracture, 260°C | 27.5 | MPa | ASTM D1708 |
| Tensile Elongation 2 | ASTM D1708 | ||
| Fracture, 23°C | 3.0 | % | ASTM D1708 |
| Fracture, 260°C | 2.0 | % | ASTM D1708 |
| Coefficient of Friction 3 | 0.16 | ||
| Wear Rate | 33 | mm/sec |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow 4(23 to 260°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Compression Molded |
| 3 . | Compression Molded |
| 4 . | Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A25 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| CP PRYME® ABS A200-29 Black | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |
| DURANEX® SF733LD | Polyplastics Co., Ltd. | PBT+SAN | DURANEX® |
| Haprez™ 3746 | Hapco Inc. | TP, Unspecified | Haprez™ |
| Karina GREEN PVC COMPOUND 861-40/36-IS-RG (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |