Ultramid® 8253 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ryQCv_Ultramid-8253-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This resin is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased flexibility. It is also available in non-heat stabilized (Ultramid 8253) and/or pigmented versions. Applications Ultramid 8253 HS is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips, fasteners, flanges, key housings as well as many flexible tubing applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.09 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.5 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.5 | -- | % | ISO 62 |
| Saturation | 8.1 | -- | % | ASTM D570 |
| Saturation, 23°C | 8.1 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.3 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 2840 | 3300 | MPa | |
| 23°C | 2300 | 730 | MPa | |
| 80°C | 400 | 370 | MPa | |
| 121°C | 295 | 220 | MPa | |
| Tensile Strength | ||||
| Yield, -40°C | 117 | 116 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 65.0 | 32.0 | MPa | ASTM D638 |
| Yield, 80°C | 25.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 20.0 | -- | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 60.0 | 32.0 | MPa | ISO 527-2 |
| Break, -40°C | 100 | 70.0 | MPa | ASTM D638 |
| Break, 23°C | 60.0 | -- | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, -40°C | 7.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.0 | 15 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 29 | -- | % | ASTM D638 |
| Yield, 121°C | 34 | 30 | % | ASTM D638 |
| Break, -40°C | 9.0 | 20 | % | ASTM D638 |
| Break, 23°C | > 100 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 40 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 3050 | 3150 | MPa | ASTM D790 |
| 23°C | 2210 | 670 | MPa | ASTM D790 |
| 65°C | 415 | -- | MPa | ASTM D790 |
| 90°C | 325 | -- | MPa | ASTM D790 |
| 121°C | 260 | -- | MPa | ASTM D790 |
| 23°C | 1900 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 148 | 141 | MPa | ASTM D790 |
| 23°C | 87.0 | 32.0 | MPa | ASTM D790 |
| 65°C | 25.0 | -- | MPa | ASTM D790 |
| 90°C | 20.0 | -- | MPa | ASTM D790 |
| 121°C | 14.0 | -- | MPa | ASTM D790 |
| 23°C | 65.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 18 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 80 | 64 | J/m | |
| 23°C | 150 J/m | No Break | ||
| Drop Impact Resistance (23°C) | 271 | > 271 | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 168 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 9.9E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 8.8E-5 | -- | cm/cm/°C | |
| Transverse | 9.3E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.710 mm | 105 | -- | °C | |
| 0.750 mm | 105 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 0.750 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 0.750 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 5111 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| TRIMMA® FT6120 | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| NOTIO™ PN-2070 | Mitsui Chemicals America, Inc. | TPE | NOTIO™ |
| Nypol® PA A3 G15 P7 M1 S1 NTLA014 NR335 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DIAREX® THH103 | PTT Global Chemical Public Company Limited | PS (GPPS) | DIAREX® |