NEXT REGRIND PA66 101L-300RG
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | NEXT Specialty Resins, Inc. |
| Trademark: | NEXT REGRIND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1rrZe2_NEXT-REGRIND-PA66-101L-300RG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEXT REGRIND PA66 101L-300RG is a Polyamide 66 (Nylon 66) material. It is available in North America. Important attributes of NEXT REGRIND PA66 101L-300RG are:
Typical application of NEXT REGRIND PA66 101L-300RG: Furniture |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 40 to 45 | g/10 min | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D790 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 87.8 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 30 TFE 15 | RTP Company | Nylon 66 | RTP |
| Rilsan® MB 3610 NAT | Arkema | Nylon 11 | Rilsan® |
| Nypol® PA A3 T30 UV NTLA010 NR434 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Andur 8500 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Karina BROWN COLOR CONCENTRATE -E 36/339-RG-G | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |