Type: Estane® AG 8451 is a polyether based aliphatic (TPU) specifically formulated to be used as an adhesive interlayer film. AG-8451 is an excellent general purpose polymer for all optical aliphatic applications. Features: This polymer works over a broad range of processing temperatures with excellent laminating results. Uses: Adhesive interlayer for glass-clad polycarbonate without a surface primer |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 3.45 | MPa | |
| 200% Strain | 8.27 | MPa | |
| 300% Strain | 13.8 | MPa | |
| Tensile Strength 2(Break) | 48.3 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 480 | % | ASTM D412 |
| Tear Strength 4 | 56.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 22°C, 22 hr | 23 | % | |
| 70°C, 22 hr | 95 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -60.0 | °C | DSC |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | Internal Method |
| TMA | Internal Method | ||
| Peak | 88 | °C | |
| Range | 65 to 130 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 5 | 1.496 | ASTM D542 | |
| Transmittance 6(1270 µm) | 85.0 to 95.0 | % | ASTM D1003 |
| Haze 7(1270 µm) | 0.0 to 0.30 | % | ASTM D1003 |
| Yellowness Index 8(1.27 mm) | < 1.0 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | Between two pieces of 1/8 inch glass |
| 6 . | Between two pieces of 1/8 inch glass |
| 7 . | Between two pieces of 1/8 inch glass |
| 8 . | Between two pieces of 1/8 inch glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3830 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| POPELEN QHCA-352S | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| Kepital® TS-22H | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Moplen HP5035 | LyondellBasell Industries | PP Homopolymer | Moplen |
| SD POLYCA™ LR8031V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |