Kynar® 460
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1pdGDu_Kynar-460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR® 460 is a semi-crystalline high molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply a grade suitable for a variety of processing requirements and end-use applications. The powder form of this resin is available as KYNAR® 461. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.77 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 75 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 34.5 to 48.3 | MPa | |
| Break, 23°C | 31.0 to 48.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 50 to 250 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1380 to 1790 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 48.3 to 62.1 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 55.2 to 68.9 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 155 to 160 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 2350 to 2950 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® 213B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Lucent PA G6-33 | Lucent Polymers, Inc. | Nylon 6 | Lucent PA |
| LUVOCOM® 1/CF/20-OS | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Osterlene® PPC-35-1.8-N | Osterman & Company | PP Copolymer | Osterlene® |
| Petrotene® PP A3 G15 NTLA010 PH307 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |