NORYL GTX™ GTX918W resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1pUcrD_NORYLGTXGTX918Wresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 1.3 - 1.6 | % | Internal method |
| Transverse flow : 3.20mm | 1.0 - 1.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 53 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2360 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 98.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 40.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 189 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 149 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 254 - 293 | °C | |
| Middle Temperature | 260 - 293 | °C | |
| Front Temperature | 266 - 293 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 500P | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Zhongfa PP ZF-UV1 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Chiao Fu PA6 MC212G50 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| ColorRx® TPE-B90A0RXCL | LTL Color Compounders, Inc. | TPE | ColorRx® |
| LNP™ THERMOCOMP™ WX05505 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |