Rilsan® BESNO 24 TL CC
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1oc80N_Rilsan-BESNO-24-TL-CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESNO 24 TL CC is a polyamide 11 produced from a renewable source. This grade with good translucence properties is designed for extrusion. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 77 | ||
| Shore D, 15 sec | 74 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1280 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 43.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, EHLN, 22-010 | ISO 1874 | |
| Renewable Carbon Conent | > 70 | % | ASTM D6866 |
| Transparency 1 | 85 | % | ISO 13168-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | 560 nm, 2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-113N40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Exxtral™ Performance Polyolefin LNT010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| ECOMID B | Nilit Plastics | Nylon 6 | ECOMID |
| LUVOCOM® 1850-7783 VP | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| LEXAN™ PC2200R resin | SABIC Innovative Plastics | PC | LEXAN™ |