DI-COAT R-4721LV/30
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | DI-COAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1oOhIk_DI-COAT-R-4721LV-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-COAT R-4721 / DI-COAT R-4721 LV (lower viscosity) Shore 90 D, room temperature curing, medium to high thixotropic coating for dielectric insulating applications. DI-COAT R-4721 is ideal for use on vertical or sloping surfaces where flow or drain-off cannot be tolerated. DI-COAT R-4721 is easy to use, and should be used on insulating applications where conformal coating is required. DI-COAT R-4721 LV exhibits similar characteristics to DI-COAT R-4721, but has a lower viscosity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D4669 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature 1 | 167 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 2(25°C) | 1.7 to 2.3 | hr | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time 3(49°C) | 4.0 to 6.0 | hr |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.10 | ||
| 100 kHz | 3.00 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.024 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 13 |
| Note Message | |
|---|---|
| 1 . | For ultimate HDT post cure an additional 6-12 hrs @ 150°C |
| 2 . | 100 g |
| 3 . | Plus 6-12 hours @ 200°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STELACOAT FA-2500/FB-2500 | DIC Corporation | PUR, Unspecified | STELACOAT |
| Nilac F17 V0 | Soredi S.p.a. | ABS | Nilac |
| Heraflex® A 90-21-90 | Radici Plastics | SEBS | Heraflex® |
| Sylvin 5170-85 White 1451 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL PPX™ PPX830 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |