VALOX™ 815F resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1o9m8Y_VALOX-815F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For foodcontact applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/5.0 kg | 70 | g/10 min | |
| 266°C/1.2 kg | 16 | g/10 min | |
| 266°C/5.0 kg | 70 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 22.0 | cm³/10min | |
| 265°C/1.2 kg | 12.0 | cm³/10min | |
| 265°C/5.0 kg | 50.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 1.0 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.26 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 195 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5500 | MPa | ASTM D638 |
| -- | 5500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 90.0 | MPa | ASTM D638 |
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Break 3 | 90.0 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4500 | MPa | ASTM D790 |
| -- 7 | 5100 | MPa | ISO 178 |
| Flexural Stress 8 | ISO 178 | ||
| -- 9 | 130 | MPa | |
| -- 10 | 145 | MPa | |
| Flexural Strain at Break 11 | 5.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 15 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 4.0 | kJ/m² | ISO 179/2C |
| 23°C 12 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 39 | J/m | ASTM D256 |
| 0°C | 39 | J/m | ASTM D256 |
| 23°C | 39 | J/m | ASTM D256 |
| -30°C 13 | 4.0 | kJ/m² | ISO 180/1A |
| 0°C 14 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 300 | J/m | ASTM D4812 |
| 23°C | 300 | J/m | ASTM D4812 |
| -30°C 16 | 25 | kJ/m² | ISO 180/1U |
| 23°C 17 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 6.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 18 | 205 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 150 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 19 | 175 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 150 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525, ISO 306/A50 13 21 |
| -- | 197 | °C | ASTM D1525, ISO 306/B50 14 22 |
| -- | 195 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 160 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 265 to 275 | °C | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Break |
| 10 . | Yield |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 mm |
| 19 . | 120*10*4 mm |
| 20 . | 80*10*4 mm |
| 21 . | Rate A (50°C/h), Loading 2 (50 N) |
| 22 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4900-611UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sylvin 60509 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| GAPEX® HT RNP38MU07BK | Ferro Corporation | Nylon+PP | GAPEX® HT |
| Geon™ Vinyl Flexible R242BE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Grilamid® XE 4028 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |