| PBT, 20 % glass fibers, injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.46 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 260°C, 2.00mm 1 | 1.4 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.10 | % | ISO 294-4 |
| Flow direction : 260°C, 2.00mm 3 | 0.50 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.10 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 100.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6650 | MPa | ASTM D638 |
| 23°C | 7100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture, 23°C | 114 | MPa | ASTM D638 |
| Fracture, 23°C | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.6 | % | ASTM D638 |
| Fracture, 23°C | 3.4 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 6900 | MPa | ISO 899-1 |
| 1000 hr | 6300 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 5700 | MPa | ASTM D790 |
| 23°C 5 | 7000 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 181 | MPa | ASTM D790 |
| 3.5% strain 6 | 190 | MPa | ISO 178/A |
| 23°C 7 | 195 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) 8 | 4.0 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| -- 9 | 11.4 | °C | IEC 60216 |
| -- 10 | 9.3 | °C | IEC 60216 |
| -- 11 | 14.0 | °C | IEC 60216 |
| Temperature index 12 | IEC 60216 | ||
| Electric Strength | 160 | IEC 60216 | |
| Tensile Impact Strength | 140 | IEC 60216 | |
| Tensile Strength | 150 | IEC 60216 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behavior 13 | passed | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GHMR, 09-070, GF20 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 140 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 215 | °C | ISO 306/B120 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 14 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.26 | W/m/K | ISO 8302 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.80 | IEC 60250 | |
| 23°C, 1 MHz | 3.60 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index 15 | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Pull Rate: 2 mm/min; 50% RH |
| 9 . | Electric Strength |
| 10 . | Tensile Impact Strength |
| 11 . | Tensile Strength |
| 12 . | 20000 h |
| 13 . | US-FMVSS302 |
| 14 . | 10°C/min |
| 15 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 330XSCd | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| GELAST 1180 | Guang Sung Plastics (GSPL) | TPV | GELAST |
| Plenco 01501 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |
| POTICON BT322 | Otsuka Chemical Co., Ltd. | PBT | POTICON |
| LNP™ COLORCOMP™ HX215HPC compound | SABIC Innovative Plastics | PBT | LNP™ COLORCOMP™ |