EPIMIX PBT IMP NC B801
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1kgd69_EPIMIX-PBT-IMP-NC-B801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EPIMIX PBT , impact modified , heat stabilized , lubricated for injection moulding. EPIMIX PBT IMP NC B801 is used in all sectors of industry, compliance with RoHs derivatives. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 2.0 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 1.8 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 76 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | 2000 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 65.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 20 | 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1900 | 1750 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 85.0 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 10 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 175 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-9305 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Geon™ Vinyl Flexible XV3906 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| PLANAC BT-6035 | TOYOBO America, Inc. | PBT | PLANAC |
| Kepital® MX20BT01 | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| XYLEX™ X5230 resin | SABIC Innovative Plastics Asia Pacific | PC+PET | XYLEX™ |