XAREC™ SP140
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1iqbno_XAREC-SP140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XAREC™ SP140 is a Syndiotactic Polystyrene (SPS) product filled with 15% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C | 0.30 to 0.70 | % | |
| Flow : 80°C | 0.20 to 0.50 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 6100 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 33 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 29 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed 2 | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 3 | 175 | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed 4 | 135 | °C | ISO 75-2/A |
| CLTE | TMA | ||
| Flow : -30 to 30°C | 3.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.1E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 50 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | < 1.0E-3 | IEC 60250 | |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 0 | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (> 1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | Mold temperature: 150°C |
| 3 . | Mold temperature: 150°C |
| 4 . | Mold temperature: 80°C |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PQ 83 N | Plastcom | PP, Unspecified | SLOVALEN® |
| NEXT REGRIND POMC TX90-100RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Nanjing Hongrui PC C1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| Kareline® PPMS5050 EC | Plasthill Oy | PP Homopolymer | Kareline® |
| LNP™ VERTON™ MV006BS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |