LIM™ 6061

Category:	Silicone Rubber, LSR , Silicone Rubber, LSR
Manufacturer:	Momentive Performance Materials Inc.
Trademark:	LIM™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	1hLxyB_LIM-6061.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LIM6061 is the next generation in 60-durometer liquid silicone rubber. It is a two-component product formulated for use in liquid injection molding to produce high performance parts. It is clear, but easily pigmentable with Momentive masterbatch colors. The combination of excellent tear strength and very high tensile strength makes this product suitable for a wide variety of applications. Mechanical parts such as connector inserts, seals, flexible mounds, and valve parts can be made readily from LIM6061 liquid silicone rubber.

Key Features and Benefits

High clarity for excellent visibility

Excellent tear strength

Convenient 1:1 mix ratio for use with automatic equipment

Rapid cure time: 10 to 40 seconds depending upon part size, configuration and molding temperature

Wide range of molding temperatures: 150°C (302°F) to 232°C (450°F)

Excellent release from metal molds

High Bayshore resilience

Potential Applications

sports goggles and masks

health care profiles

camera parts

coating metal rolls

General Information
Features	Fast Cure Good Mold Release Good Tear Strength High Clarity High Tensile Strength
Uses	Camera Applications Coating Applications Connectors Medical/Healthcare Applications Seals Sporting Goods Valves/Valve Parts
Agency Ratings	BfR Food Contact, Unspecified Rating FDA 21 CFR 177.2600 USP Class VI
UL File Number	E205753
Appearance	Clear/Transparent
Forms	Liquid
Processing Method	Liquid Injection Molding (LIM)

Elastomers	Nominal Value	Unit
Bayshore Resilience
-- ¹	63	%
-- ²	65	%

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Thermoset	Nominal Value	Unit
Thermoset Components
Part A	Mix Ratio by Weight: 1.0
Part B	Mix Ratio by Weight: 1.0

Cured Properties	Nominal Value	Unit
Shore Hardness
Shore A ³	60
Shore A ⁴	60
Tensile Modulus
100% Secant ⁵	2.40	MPa
100% Secant ⁶	2.70	MPa
Tensile Strength
-- ⁷	6.60	MPa
-- ⁸	9.40	MPa
Tensile Elongation at Break
-- ⁹	400	%
-- ¹⁰	470	%
Compression Set ¹¹(177°C, 22.0 hr)	27	%
Tear Strength
Die B ¹²	6.60	kN/m
Die B ¹³	40.3	kN/m

Note Message
1 .	Press Cure 17 min @ 177°C (350°F)
2 .	Postbaked 4 hr @ 205°C (400°F)
3 .	Postbaked 4 hr @ 205°C (400°F)
4 .	Press Cure 17 min @ 177°C (350°F)
5 .	Press Cure 17 min @ 177°C (350°F)
6 .	Postbaked 4 hr @ 205°C (400°F)
7 .	Postbaked 4 hr @ 205°C (400°F)
8 .	Press Cure 17 min @ 177°C (350°F)
9 .	Postbaked 4 hr @ 205°C (400°F)
10 .	Press Cure 17 min @ 177°C (350°F)
11 .	Press Cure 17 min @ 177°C (350°F)
12 .	Postbaked 4 hr @ 205°C (400°F)
13 .	Press Cure 17 min @ 177°C (350°F)

Resin Grade	Manufacturer	Category	Trademark
DINAPLEN® PPH1S05 M203	Grupo Repol	PP Homopolymer	DINAPLEN®
Huafon HF-3098A	Huafon Group Co., Ltd.	TPU-Polyester	Huafon
LAPEROS® E480i	Polyplastics Co., Ltd.	LCP	LAPEROS®
Iupilon® MB6001UR	Mitsubishi Engineering-Plastics Corp	PC+Acrylic	Iupilon®
3M™ Dyneon™ Fluoroelastomer FPO 3631	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer