RTP 407
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1h2kDx_RTP-407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass Fiber reinforced polystyrene offers significant improvements in strength, moduli and dimensional stability over the base resin. The series of materials has very little tensile elongation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 82.7 | MPa | ASTM D638 |
| -- | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 128 | MPa | ASTM D790 |
| Yield | 131 | MPa | ASTM D790 |
| Compressive Strength | 121 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 160 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.32 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | ASTM D150 | |
| Arc Resistance (1.59 mm) | 40.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, 0.25in: 1 mil/ina |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 28420 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| ColorRx® PEEK-3000RX | LTL Color Compounders, Inc. | PEEK | ColorRx® |
| DINALON® B1S25 G15 | Grupo Repol | Nylon 6 | DINALON® |
| Hostacom 68F4-3 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Diakon® CTG635 | Lucite International Holland BV | Acrylic (PMMA) | Diakon® |