This data represents typical values that have been calculated from all products classified as: Generic PEKK This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 to 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.10 to 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 86 to 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3450 to 4510 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 6.96 to 123 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 11 to 80 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3380 to 4570 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 103 to 207 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 to 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 to 189 | °C | ASTM D648 |
| Glass Transition Temperature | 155 to 163 | °C | DSC |
| Melting Temperature | 306 to 360 | °C | DSC |
| CLTE - Flow | 2.1E-5 to 8.4E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIG4002 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| EMOPLEN® A 1503 T4 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| PIVINEL™ 126-D1 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| MACOMASS PP MM-PP HI 84 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| EnviroPro 2010 | West Michigan Compounding | PP Copolymer | EnviroPro |