Flexalloy® 9100-75
| Category: | PVC Elastomer , Polyvinyl Chloride Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Flexalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gpcvf_Flexalloy-9100-75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexalloy®9100-75 is a polyvinyl chloride elastomer (PVC elastomer) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Flexalloy®The main features of 9100-75 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 - 2.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Fracture | 18.6 | MPa | ASTM D638 |
| 100% strain | 8.27 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 36.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 26 | % | ASTM D395 |
| 70°C, 22 hr | 55 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 80.0 | °C | ASTM D794 |
| Brittleness Temperature | -48.0 | °C | ASTM D746 |
| Additional Information |
|---|
| 脆化温度，ASTM D746：<-48°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 182 - 199 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa | |
| Screw L/D Ratio | 20.0 : 1.0 - 24.0 : 1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ500 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Trademark PE LD2920B | Trademark Plastics Corporation | LDPE | Trademark PE |
| DIAMALOY ENGINEERED ALLOYS 808 C8 WW | Network Polymers, Inc. | PC Alloy | DIAMALOY ENGINEERED ALLOYS |
| Kumho KNB 25M | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Jiangsu Sinarise JM8011 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |