OmniLon™ PA6/6 U GMR36 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gldVG_OmniLon-PA6-6-U-GMR36-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 36% Glass/Mineral Reinforced, Utility Grade, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 123 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPC-20T Black | PolyOne Corporation | PP Copolymer | Maxxam™ |
| CAPXIDAN™ HD | NWP, Inc. | Ethylene Copolymer | CAPXIDAN™ |
| Delta N66R-1G31 | Delta Polymers | Nylon 66 | Delta |
| Karina CLEAR PVC COMPOUND -E 75/244-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| REV Materials 8007 | REV Materials | Polyolefin, Unspecified | REV Materials |