TRISTAR® PC-10FRN(V)
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | TRISTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gRaUb_TRISTAR-PC-10FRN-V-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRISTAR®PC-10FRN(V) is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. TRISTAR®The application fields of PC-10FRN(V) include electrical/electronic applications and wire and cable. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 75 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 590 | J/m | ASTM D256 |
| Tensile Impact Strength (3.17 mm) | 443 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 134 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C 1 | 6.0E+15 | ohms·cm | ASTM D257 |
| 90°C 2 | 3.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.17E-6 mm) | 24 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 2.50 mm | PLC 1 | UL 746 | |
| 3.00 mm | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 2.50 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm, BK, GY, BG | 5VA | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 254 - 274 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 293 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Injection Pressure | 75.8 - 124 | MPa | |
| Back Pressure | 0.345 - 1.38 | MPa |
| Injection instructions |
|---|
| Injection Speed - Edge Gate: Slow to MediumInjection Speed - Tab Gate: Medium to FastInjection Speed - Tunnel Gate: Fast |
| Note Message | |
|---|---|
| 1 . | 40 hr, 50% RH |
| 2 . | 96 hr, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 2500-WH10 | Prime PVC® | PVC, Rigid | Prime |
| VENYL SN070 | AD majoris | Nylon 6 | VENYL |
| Bormed™ RJ880MO | Borealis AG | PP Random Copolymer | Bormed™ |
| Hanwha Total PP TH54M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina WHITE PVC COMPOUND -E 807-10/203-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |