Iupilon® MB2210R
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1dlxxD_Iupilon-MB2210R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® MB2210R is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® MB2210R: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 8.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Water Absorption (Saturation, 23°C) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.3 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 34 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 220 to 250 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP218R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Hanwha Total PP SI83R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LNP™ THERMOCOMP™ QF006 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| Petrothene® NA209009 | LyondellBasell Industries | LDPE | Petrothene® |
| Starex TX-0550 | LOTTE ADVANCED MATERIALS CO., LTD. | MABS | Starex |