Viton® A-500
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DuPont Performance Elastomers |
| Trademark: | Viton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1dI8Su_Viton-A-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Viton A-500 fluoroelastomer is a new generation "A-family" gum polymer that provides improved processing when compared with existing fluoroelastomers. Viton A-500 is designed for use with the clean molding bisphenol curative, Viton Curative No. 50. Compared to "A-family" dipolymers, Viton A-500 provides: -Improved compression molding -Better mold release -Less mold fouling -Faster cure rate -Improved compression set resistance Applications -Compression and transfer molding --O-rings --gaskets --seals -Profile extrusion -Calendered goods |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 7.20 | MPa | ASTM D412 |
| Tensile Strength (Break) | 15.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 200 | % | ASTM D412 |
| Compression Set | |||
| 200°C, 22 hr | 9.0 | % | ASTM D395B |
| 200°C, 70 hr | 14 | % | ASTM D395 |
| 200°C, 336 hr | 26 | % | ASTM D395B |
| 232°C, 70 hr | 31 | % | ASTM D395B |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| 275°C, 70 hr | -20 | % | ASTM D573 |
| 100% strain, 275°C, 70 hr | -22 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (275°C, 70 hr) | 5.1 | % | ASTM D573 |
| Change in Durometer Hardness in Air (support a, 275°C, 70 hr) | 0.0 | ASTM D573 |
| Additional Information |
|---|
| Mooney Scorch, MS at 121°C, Minimum: 47Mooney Scorch, MS at 121°C, 1 unit rise: 30 minODR at 177°C, Microdie, 3° Arc, 12 min:ML: 17 in-lbts2: 1.5 mint90: 2.9 minMH: 123 in-lbNominal Viscosity, ML 1 + 10, 121°C: 50Polymer Fluorine Content: 66% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer N-500 | Shanghai Potomer International Trade Co., Ltd. | CPVC | Shanghai Potomer |
| BJB Silicone TC-5045 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| AVP™ GY601CP | SABIC Innovative Plastics | Nylon 6 | AVP™ |
| Enviramid® N1335STHL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| EPAMOULD 250D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |